Welcome! [Sign in] [Register]     Contact us 400-888-6037
Plastic housing > Plastic housing > PBT black housing > Insert Bearing Plastic Housing T206
Visited Products
Insert Bearing Plastic Housing T206
Goods ID:140000521
Original price:$3.52Price notification
Stock:200 Pcs
I want to buy:-+Pcs
Selected " 1Pcs "
Add to Cart
Search similar goods
If the stock purchase quantity insufficient number please click:
If the product you want is not Listed please click:

Product parameters

Goods ID: 140000521 Brand: NETMALL
Category: PBT black housing Weight:(g) 230.00
Bearing seat model: T206 Color: Black
Bearing seat type: 立式座P Operating characteristic:
I.D. for Inset Bearing with Housing:(mm) Spherical Diameter:(mm) 62
Bearing seat molding method : Casting Plastic Bearing seat material: PBT
Supporting bearing UC206    

Product Feature

Plastic seat with light weight, easy to install, maintenance-free properties, while cushioning the impact resistance with commonly used cast iron seat or do not have the punch holder


Bearings supporting plastic seat

Product Details

Plastic housing Product Description

Plastic seat with unique light weight, easy to install, maintenance-free , but with a common cast iron seat or seats that are not stamped with a damping impact resistance. With the continuous development of new materials , plastic seat being increasingly widely used in engineering . For different situations , plastic spherical bearing can be POM, HDPE, PP, UPE, PTFE and other different materials, commonly used PBT plastic housing material .

PBT Introduction

Poly (butylene terephthalate) , the English name polybutylece terephthalate ( referred to as PBT), a polyester series , is a 1.4 - butanediol (1.4-Butylene glycol) and terephthalic acid (PTA) or dimethyl terephthalate ester (DMT) poly condensation, and made ​​through the mixing process is translucent to opaque white , crystalline thermoplastic polyester resin. Collectively together with PET thermoplastic polyester , or polyester.

The advantages of this material : a toughness good , not broken .

                    Note 2 streams good performance , easy molding .

                   3 relatively inexpensive phenolic material

The disadvantage of this material : no heat , when the temperature deformation

PBT physicochemical properties

PBT is translucent to opaque white , crystalline thermoplastic polyester. With high heat resistance, toughness , fatigue resistance , self-lubricating , low friction coefficient , weather resistance , low water absorption , only 0.1 % in wet conditions remain variety of physical properties ( including electrical properties ) , electrical insulation, but volume resistivity and dielectric loss big . Heat water, alkalis, acids, oils , halogenated hydrocarbons but are vulnerable to erosion , poor water resistance , low temperature can be rapidly crystallized, forming good . The disadvantage is that the notched impact strength low mold shrinkage . Therefore, most of the glass fiber reinforced or modified inorganic filler , the tensile strength, flexural strength can be increased more than doubled, heat distortion temperature also greatly improved. You can work long at 140 ℃, glass fiber reinforced products after longitudinal and transverse shrinkage consistent , easy to make products warpage.

PBT Process

PBT thermoplastic polyester plastics can be called , is applicable to different processing industries , the general number of additives are added or blended with other plastics , as additives in different proportions , can produce different specifications. PBT has the heat resistance, weather resistance, chemical resistance , good electrical properties , low water absorption , good luster, widely used in electronic appliances, auto parts, machinery , household goods , etc., and PBT products and with PPE, PC, POM, PA and so were called the five pan with plastic .

PBT crystallization speed , the most suitable processing method for injection molding, as well as other methods of extrusion, blow molding, coating and various secondary processing molding , molding required before pre-drying , moisture content should be reduced to 0.02 %.

PBT injection molding process characteristics and process parameters can be set :

PBT polymerization process maturity, low cost, easy molding. Unmodified PBT poor performance , the practical application of PBT to be modified , in which glass fiber reinforced modified grades accounted for more than 70% PBT 's .

1 PBT technology features of

PBT has a sharp melting point , melting point of 225 ~ 235 ℃, is a crystalline material , the degree of crystallinity of up to 40 %.

PBT melt viscosity is not as affected by temperature shear stress so much so , in injection molding , injection pressure PBT melt flow impact is obvious .

PBT fluidity in the molten state , low viscosity, second only to nylon molding prone to " cast " phenomenon.

PBT molding products anisotropy. PBT at high water readily biodegradable .

2 injection molding machine

Selection of the screw -type injection molding machine. Should consider the following points .

① products should be controlled by feeding 30% to 80% of the injection molding machine rated maximum amount . Not with a large injection molding machine to produce small products.

② should use tapered screw three sections , the aspect ratio of 15 to 20 , the compression ratio of 2.5 to 3.0.

③ should use self-locking nozzle and heating temperature control device .

④ When the forming flame retardant PBT, injection molding machine related parts should embalmed .

3 product and mold design

① thickness of the article should not be too thick , PBT is very sensitive to the gap , so the transition at right angles and other products should be used to connect the arc .

② unmodified PBT molding shrinkage rate of the larger , 1.7 % ~ 2.3% , have a certain mold stripping slope .

③ mold needs to vent or exhaust ducts located .

④ gate diameter should be larger.

⑤ mold temperature control device to be set . High mold temperatures can exceed 100 ℃.

⑥ Flame Retardant PBT molding, the mold surface to chrome to corrosion .

4 raw material preparation

Dried prior to injection , to control the moisture content below 0.02%. When using hot air drying cycle , when the temperature is 105 ℃, 120 ℃ or 140 ℃ , the time corresponding to no more than 6h, 4h, 2h. Material thickness less than 30mm.

Five injection molding process parameters

① PBT injection temperature decomposition temperature of 280 ℃, and actual production is generally controlled between 235 ~ 245 ℃.

② injection pressure, injection pressure is generally 50 ~ 100MPa.

③ injection rate PBT cooling speed , and therefore faster injection rate.

④ screw speed and back pressure molding PBT screw speed should not exceed 80r/min, generally between 25 ~ 60r/min. Back pressure is generally 10% to 15% of the injection pressure .

⑤ mold temperature control in 70 ~ 80 ℃, the temperature of each part of the difference does not exceed 10 ℃.

⑥ molding cycle under normal circumstances is 15 ~ 60 s.

6 Precautions

① the use of recycled material and new material proportion of recycled materials is generally 25% to 75%.

② use of the releasing agent is not used under normal circumstances the release agent, silicone release agent may be used when necessary .

③ stop processing PBT downtime in less than 30min, can be shut down when the temperature drops to 200 ℃. After a long shutdown of production , the material inside the barrel emptying want , then add new material to normal production .

④ products after processing generally does not require treatment , if necessary, treatment 1 ~ 2h at 120 ℃, .